| 航空锻件常见表观缺陷及其控制研究 |
| Study on Control of Common Appearance Defects of Aviation Forgings |
| |
| DOI：10.3969/j.issn.1674-6457.2022.10.004 |
| 中文关键词: 航空锻件 锻造缺陷 折叠 裂纹 |
| 英文关键词: air forgings forging defects fold crack |
| 基金项目: |
| Author Name | Affiliation | | SUN Chao-yuan | College of Materials Science and Engineering Chongqing Key Laboratory of Advanced Mold Intelligent Manufacturing, Chongqing University, Chongqing 400044, China
China National Erzhong Group Deyang Wanhang Die Forging Co., Ltd., Sichuan Deyang 618000, China | | ZHOU Jie | College of Materials Science and Engineering Chongqing Key Laboratory of Advanced Mold Intelligent Manufacturing, Chongqing University, Chongqing 400044, China | | ZHAO Bo | Shenyang Aircraft Design and Research Institute, Shenyang 110034, China | | JIANG Jia-jun | College of Materials Science and Engineering Chongqing Key Laboratory of Advanced Mold Intelligent Manufacturing, Chongqing University, Chongqing 400044, China
China National Erzhong Group Deyang Wanhang Die Forging Co., Ltd., Sichuan Deyang 618000, China | | XIE Jing | China National Erzhong Group Deyang Wanhang Die Forging Co., Ltd., Sichuan Deyang 618000, China | | LIU Yang | China National Erzhong Group Deyang Wanhang Die Forging Co., Ltd., Sichuan Deyang 618000, China |
|
| Hits: 2037 |
| Download times: 1045 |
| 中文摘要: |
| 目的 揭示服役寿命长、工况苛刻、锻造成本高、质量控制难度大的航空结构件与发动机盘件用钛合金、高温合金等锻件外观缺陷的产生原因及控制措施。方法 按照航空锻件锻造流程(开坯、制坯、模锻和锻后热处理)，分别研究裂纹、折叠、错移等锻造缺陷产生的原因。结果 航空锻件产生表观质量缺陷的原因一般由工艺设计不合理、锻造操作不当、工装设备保障不到位等导致，需结合锻件材料、形状、变形过程等采取对应措施进行优化解决。结论 对航空锻件缺陷产生原因进行了研究，给出了行之有效的解决措施，对于航空锻件质量的提高，尤其是新材料、大尺寸、复杂结构的航空锻件研制具有重要的工程指导意义。 |
| 英文摘要: |
| The work aims to reveal the causes and control measures of appearance defects in forging links of titanium alloy and superalloy forgings for aviation structural parts and engine parts with long service life, harsh working conditions, high forging cost and difficult quality control. According to the forging process of aviation forgings (blank opening, blank making, die forging and post forging heat treatment), the causes of forging defects such as crack, folding and dislocation are studied, respectively. The appearance quality defects of aviation forgings are usually caused by unreasonable process design, improper forging operation and inadequate equipment support. It is necessary to take corresponding measures to optimize combined with the forging material, shape and deformation process. In this paper, the causes of aviation forging defects are studied, and effective solutions are given, which has important engineering guiding significance for improving the quality of aviation forgings, especially for the development of aviation forgings with new materials, large-size and complex mechanisms. |
|