| 动态碳配分对先进高强钢组织与力学性能的影响 |
| Influences of Dynamic Carbon Partitioning Process on Microstructure Development and Mechanical Properties of Advanced High Strength Steel |
| Received:June 25, 2018 Revised:July 10, 2018 |
| DOI：10.3969/j.issn.1674-6457.2018.04.019 |
| 中文关键词: 先进高强钢 热冲压 动态碳配分 残余奥氏体 碳含量 |
| 英文关键词: AHSS hot stamping dynamic carbon partitioning retained austenite carbon content |
| 基金项目:国家自然科学基金（51034009） |
| Author Name | Affiliation | | ZHANG Fei-bao | Guangdong Institute of Aeronautics and Astronautics Equipment & Technology, Zhuhai 519090, China | | LI Xin | Nanchang Hangkong University, Nanchang 330063, China | | SONG Hong-wu | Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China | | ZHANG Shi-hong | Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China | | FAN Hai-sheng | Beijing Zhongke Pujin Special Materials and Technology Development Co., Ltd., Beijing 100081, China |
|
| Hits: 4753 |
| Download times: 3344 |
| 中文摘要: |
| 目的 为了使钢表现出更好的吸能特性，以具有较高的强度以及较好的塑性。方法 提出了一种新型一步法成形碳配分一体化工艺，即热冲压-动态碳配分(HS-DP)工艺。所提出的HS-DP工艺采用盐浴热处理的方式进行物理模拟。采用扫描电子显微镜(SEM)、X射线衍射(XRD)和拉伸试验等方法，研究了新工艺中的冷却速率对低碳先进高强钢的微观组织和力学性能的影响。针对冷却速率对残余奥氏体含量的影响进行了分析，重点研究了残留奥氏体的体积分数和碳含量对钢伸长率的影响。结果 经过HS-DP工艺处理的钢显微组织主要由初始淬火态马氏体相、最终淬火态马氏体相和残余奥氏体相共存组成。结论 实验钢表现出优异性能，说明了热冲压动态碳配分工艺前景广阔。 |
| 英文摘要: |
| This paper aims to make steel exhibit attractive properties as high strength and good ductility. A novel one step method for forming Q & P integration-Hot Stamping-Dynamic Partitioning (HS-DP) process was proposed. The proposed HS-DP process was simulated with salt bath heat treatment. The effect of microstructrue and mechanical properties in a low-carbon AHSS with different cooling rate of the new process was investigated with scanning electron microscopy (SEM), X-ray diffraction (XRD) and tensile test methods. The impact of retained austenite was also discussed, especially the influences of elongation caused by various retained austenite volume fraction and carbon-content. Microstructure of the steel subjected to HS-DP treatment was mainly composed of initial quenched martensite phase, final quenched martensite phase, final quenched martensite phase and retained austenite phase formed. This experiment steel illustrates the promising used in hot stamping dynamic carbon partitioning process. |
|