| 硼钢热冲压模具CAE顺序耦合建模及强度校核 |
| CAE Sequential Coupling Modeling and Strength Checking of Hot Stamping Die for Boron Steel |
| Received:December 13, 2016 Revised:January 10, 2017 |
| DOI：10.3969/j.issn.1674-6457.2017.01.015 |
| 中文关键词: 热冲压 模具 热-力耦合 强度 |
| 英文关键词: hot stamping mold thermo-mechanical coupling strength |
| 基金项目: |
| Author Name | Affiliation | | WANG Zhi-chao | 1.Shanghai Jiao Tong University, Shanghai 200240, China
2.Shanghai Key Laboratory of Digital Manufacturing for Complex Thin-Walled Structure, China | | LI Yong-feng | 1.Shanghai Jiao Tong University, Shanghai 200240, China
2.Shanghai Key Laboratory of Digital Manufacturing for Complex Thin-Walled Structure, China | | LUO Ai-hui | 1.Baoshan Iron and Steel Co., Ltd., Shanghai 201900, China
2.State Key Laboratory of Development and Application Technology of Automotive Steels, Shanghai 201900, China | | WAN Yong-hong | SAIC-GM-Wuling Automobile Co., Ltd., Liuzhou 545007, China | | LI Shu-hui | 1.Shanghai Jiao Tong University, Shanghai 200240, China
2.Shanghai Key Laboratory of Digital Manufacturing for Complex Thin-Walled Structure, China |
|
| Hits: 4999 |
| Download times: 4385 |
| 中文摘要: |
| 目的 针对热冲压模具开裂的问题，提出一种模具强度校核方法。方法 借助有限元仿真软件ABAQUS，对B柱进行循环仿真，获取稳定变化的模具温度场；借助专业成形软件Dynaform完成B柱成形、保压过程的仿真，获取模具和板料间的节点接触力；将模具温度场和节点接触力作为边界条件进行模具强度仿真分析。结果 模具的危险区域是模具内部靠近圆角的流道交接处，此处因为承受强烈的热冲击存在交变拉应力作用，同时又因为加工缺陷存在应力集中，是疲劳裂纹最容易萌生的地方。结论 CAE顺序耦合仿真能准确高效地计算热冲压模具的温度场、热-机械耦合应力场，分析模具的危险区域，指导模具的设计和加工，延长模具使用寿命。 |
| 英文摘要: |
| In order to prevent the crack of hot stamping die, created a method to check its strength. Using the ABAQUS to simulate thermal field of the hot stamping die; using Dynaform to get the node contact force between blank and mold; treat the thermal field and contact force as boundary conditions to analyze the mold strength. The weak area of the mold is the junction of the cooling channel where close to the fillet. The weak area suffers from alternating tensile stress under the serious thermal shock. At the same time, some manufacturing defect that results in stress concentration tends to occur at the junction. As a result, the junction of the mold cooling channel close to fillet is most likely to fatigue. CAE coupling simulation method can calculate the thermal field and thermo-mechanical coupling stress field of hot stamping mold in high accuracy and efficiency. We can use it to analyze the dangerous area of mold and give instruction for the design and manufacturing of the molds to extend the service life. |
|