文章摘要
轧制压下量对连挤连轧铜排组织和性能的影响
Effects of Rolling Reduction on Microstructure and Properties of Copper Strips during Continuous Extrusion and Rolling
Received:May 16, 2015  Revised:July 10, 2015
DOI:10.3969/j.issn.1674-6457.2015.04.001
中文关键词: 铜排  连挤连轧  轧制压下量  组织与性能
英文关键词: copper strip  continuous extrusion and rolling  rolling reduction  microstructure and properties
基金项目:国家自然科学基金(51175055);高等学校博士学科点专项科研基金博导类资助(20132124110003)
Author NameAffiliation
YUN Xin-bing Engineering Research Centre of Continuous Extrusion, Ministry of Education,Dalian Jiaotong University, Dalian 116028, China 
WANG Cong Engineering Research Centre of Continuous Extrusion, Ministry of Education,Dalian Jiaotong University, Dalian 116028, China 
TIAN Tian Engineering Research Centre of Continuous Extrusion, Ministry of Education,Dalian Jiaotong University, Dalian 116028, China 
ZHAO Ying Engineering Research Centre of Continuous Extrusion, Ministry of Education,Dalian Jiaotong University, Dalian 116028, China 
PEI Jiu-yang Engineering Research Centre of Continuous Extrusion, Ministry of Education,Dalian Jiaotong University, Dalian 116028, China 
Hits: 4579
Download times: 4529
中文摘要:
      目的 连挤连轧是一种带材生产新技术,它结合连续挤压与热轧工艺的特点,研究轧制压下量对连挤连轧铜排组织、性能的影响。 方法 利用光学显微镜、万能材料实验机、布氏硬度仪对铜排连挤连轧的组织、性能进行试验研究。 结果 经连续挤压的铜排为等轴再结晶组织,平均晶粒尺寸为 60 μm 左右,抗拉强度为 220 MPa,延伸率为 66% ,沿铜排宽度方向的硬度分布不均匀。 连挤连轧后的铜排晶粒沿轧制方向被拉长成扁平状,随着轧制压下量的增加,相邻晶界间距减小,最终形成纤维组织,沿铜排宽度方向的硬度分布较连续挤压排坯均匀。 当压下量由 2 mm 增加到 8mm 时,铜排的抗拉强度由 250 MPa 增加到 400 MPa,延伸率由 48% 降低到 13% ,硬度由 72HB 左右增加到 119HB。 结论 得到了轧制压下量对连挤连轧铜排组织和性能的影响规律。
英文摘要:
      The aim of this study was to investigate effects of rolling reduction on microstructure and properties of copper strips during continuous extrusion and rolling which was a new strip production technology combining the features of continuous extrusion and hot rolling. The microstructure and properties of copper strip during continuous extrusion and rolling were investigated by using optical microscopy, universal testing machine and Brinell hardness measurement. The results indicated that recrystallized grains were obtained by continuous extrusion, the average grain size, the tensile strength, and elongation were about 60 μm, 220 MPa and 66% respectively, and the hardness distribution along the width of the copper strip was not uniform. The grains were elongated during continuous extrusion and rolling. With the rolling reduction increased, the adjacent grain boundaries spacing gradually decreased and the microstructures of copper strip gradually formed fibrous tissues, and hardness distribution became more uniform along the width direction of copper strip. The tensile strength increased from 250 MPa to 400 MPa, the elongation decreased from 48% to 13% and the hardness increased from 72HB to 119HB when the rolling reduction increased from 2 mm to 8 mm. The influence pattern of rolling reduction on microstructure and properties of copper strips during continuous extrusion and rolling was obtained.
View Full Text   View/Add Comment  Download reader
Close

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

You are the503317visitor    渝ICP备15012534号-6

>Copyright:Journal of Netshape Forming Engineering 2014 All Rights Reserved

>Postal Code: Phone:Fax: Email:

>    

渝公网安备 50010702501719号