夏琴香,江鹏,肖刚锋,等.镁合金带内筋筒形件热强旋成形质量及参数优化[J].精密成形工程,2022,14(5):1-7.
XIA Qin-xiang,JIANG Peng,XIAO Gang-feng,et al.Forming Quality and Parameters Optimization for Hot Power Spinning of Magnesium Alloy Cylindrical Parts with Inner Ribs[J].Journal of Netshape Forming Engineering,2022,14(5):1-7. |
| 镁合金带内筋筒形件热强旋成形质量及参数优化 |
| Forming Quality and Parameters Optimization for Hot Power Spinning of Magnesium Alloy Cylindrical Parts with Inner Ribs |
| |
| DOI：10.3969/j.issn.1674-6457.2022.05.001 |
| 中文关键词: ZK61镁合金 带内筋筒形件 正交试验 热强旋 灰色关联度 |
| 英文关键词: ZK61 magnesium alloy cylindrical parts with inner ribs orthogonal test hot power spinning grey relational degree |
| 基金项目:国家自然科学基金(51775194) |
|
| 摘要点击次数: 2471 |
| 全文下载次数: 800 |
| 中文摘要: |
| 目的 探明镁合金带内筋筒形件热强旋成形质量影响因素间的相互作用，并获得优化后的内筋数量及工艺参数。方法 设计了五因素、三水平正交试验方案，开展了灰色关联度分析及极差分析，研究了内筋数量及工艺参数对旋压件直线度、圆度、筋背凹陷率、内筋饱和度、筋高不均匀度等成形质量指标影响的主次顺序，获得了最优的参数组合。结果 各参数对旋压件成形质量的综合影响主次顺序为:内筋个数N＞管坯壁厚t0＞减薄率ψt＞成形温度T＞进给比f，最优的参数组合为N=12、t0=8 mm、ψt=70%、T=350 ℃、f=0.4 mm/r。结论 通过在最优的参数组合下开展热强旋试验，可制备出质量合格的镁合金带内筋筒形件。 |
| 英文摘要: |
| This work aims to explore the interaction among influence factors of forming quality for hot power spinning of magnesium alloy cylindrical parts with inner ribs (CPIRs), and obtain the optimized inner rib number and processing parameters. A five-factor, three-level orthogonal test scheme was designed, the grey correlation analysis and range analysis were conducted, the influence of inner rib number and processing parameters on the forming quality indexes, such as straightness, roundness, concave ratio of the back of rib, saturation degree of inner ribs and inhomogeneity degree of inner ribs, the optimal parameter combination was obtained. The results show that the primary and secondary order of the comprehensive influence of various parameters on the forming quality of spun workpiece is:number of inner ribs N > wall thickness of cylindrical blank t0> thinning rate of wall thickness ψt > forming temperature T> roller feed rate f, and the optimal parameters combination is:N=12, t0=8 mm, ψt=70%, T=350 ℃, f=0.4 mm/r. Under the optimal parameters combination, the magnesium alloy CPIRs with qualified forming quality can be prepared by hot power spinning. |
|