蔡圳武,詹艳然.旋轮进给率对小锥角锥形件表面形貌及显微组织的影响[J].精密成形工程,2019,11(3):133-137.
CAI Zhen-wu,ZHAN Yan-ran.Influences of Spinning Roller Feed Rate on Surface Morphology and Microstructure of Conical Parts with Small Angle[J].Journal of Netshape Forming Engineering,2019,11(3):133-137.
旋轮进给率对小锥角锥形件表面形貌及显微组织的影响
Influences of Spinning Roller Feed Rate on Surface Morphology and Microstructure of Conical Parts with Small Angle
投稿时间:2019-03-31  修订日期:2019-05-10
DOI:10.3969/j.issn.1674-6457.2019.03.016
中文关键词: 锥形件  旋压  进给率  表面形貌  显微组织
英文关键词: conical parts  spinning  feed rate  surface morphology  microstructure
基金项目:
作者单位
蔡圳武 福州大学 机械工程及自动化学院福州 350116 
詹艳然 福州大学 机械工程及自动化学院福州 350116 
摘要点击次数: 3965
全文下载次数: 2873
中文摘要:
      目的 通过旋压工艺试验,考察旋轮进给率对锥形件表面质量的影响,探讨表面缺陷的形成机理。方法 采用4个不同的旋轮进给率分别进行旋压试验,在扫描电镜下观察其表面形貌及腐蚀后的显微组织,分析其表面形貌变化规律、晶粒尺寸分布情况,并与初始表面形貌及显微组织进行对比分析。结果 进给率越大,表面波纹越明显,板坯表层金属被旋轮剥离越严重且晶粒大小分布越不均匀;进给率较小时,锥形件表面光滑,且晶粒大小分布均匀。结论 进给率对表面造成缺陷的形成机理是表层金属被剥离,表面波纹是导致晶粒大小分布不均匀的原因。
英文摘要:
      The paper aims to investigate the influences of spinning roller feed rate on surface quality of conical parts by spinning process test, and to explore the formation mechanism of surface defects. Four different spinning roller feed rates were used for spinning test; and the surface morphology and microstructure after corrosion were observed under scanning electron microscopy; the variation of surface morphology and the grain size distribution were analyzed and compared with the initial surface morphology and microstructure. The results show that when the feed rate was large, the surface ripples were more obvious, the surface metal was more severely scraped by the roller, and the grain sizes were more uneven; and accordingly, the smaller the feed rate, the more smooth the cone surface, and the more even the grain sizes. The formation mechanism of the defect caused by the feed rate is that the surface metal is scraped off. The cause of uneven grain size distribution is the surface ripples.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第14775241位访问者    渝ICP备15012534号-4

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

    

渝公网安备 50010702501719号