万元元,贾俞军,李强,等.铸锻复合成形AZ91D摩托车发动机壳体热处理工艺研究[J].精密成形工程,2012,4(4):1-9.
WAN Yuan-yuan,JIA Yu-jun,LI Qang,et al.Research on Heat Treatment of AZ91D Motorcycle Engine Shell Produced by Compound Forming of Die-casting and Forging[J].Journal of Netshape Forming Engineering,2012,4(4):1-9. |
| 铸锻复合成形AZ91D摩托车发动机壳体热处理工艺研究 |
| Research on Heat Treatment of AZ91D Motorcycle Engine Shell Produced by Compound Forming of Die-casting and Forging |
| 投稿时间：2012-05-25 修订日期：2012-07-10 |
| DOI： |
| 中文关键词: 液态铸锻双控成形 AZ91D镁合金 热处理 显微组织 力学性能 |
| 英文关键词: compound forming of casting and forging AZ91D magnesium alloy heat treatment microstructure mechanical property |
| 基金项目: |
|
| 摘要点击次数: 4264 |
| 全文下载次数: 3076 |
| 中文摘要: |
| 采用不同固溶和时效热处理工艺对液态铸锻双控成形AZ91D摩托车发动机壳体进行了热处理实验。结果表明：样品经过T4（415 ℃×9 h, 60 ℃水淬）处理后，合金的抗拉强度和延伸率最大，其值为239.7 MPa、1.58%，较未热处理提高幅度分别为41.6%,79.9%。经T6（415 ℃×9 h，60 ℃水淬+205℃×16 h，空冷）处理后，样品显微组织中的第二相得到均化，在一定程度上强化了合金。未处理态、T4、T6状态下的拉伸试样断口形貌中均存在较多的韧窝，表明铸锻双控成形制件的塑性较好。T6（415℃×9 h，60 ℃水淬）热处理后的拉伸试样断口形貌中韧窝最多，塑性最好。 |
| 英文摘要: |
| Microstructures and mechanical properties of an AZ91D magnesium alloy motorcycle engine shell prepared with compound forming (die-casting plus forging) were characterized in various heat treatment conditions. Results show that The ultimate tensile strength and elongation of test samples were up to 239.7 MPa，1.58% after solution processing (415 ℃×9 h， 60 ℃ water-quenching)，which have been improved 41.6% and 79.9%，compared with no heat processing. And the microstructures of test samples were uniformed after solution and age treatment (415 ℃×9 h， 60 ℃ water-quenching+205 ℃×16 h，dry quenching) and the alloy was strengthened to a certain extent. Lots of dimples have been found in the fracture morphology of tensile specimens at no heat treatment，T4 and T6 state，which shows that the parts which are produced by compound forming of die-casting and forging have relatively high plasticity. The fracture morphology of tensile specimen after T6 (415 ℃× 9 h, 60 ℃ water quenching) heat treatment have the largest number of dimples，and shows the best plasticity. |
|