姜春茂,潘玲,赵广军,等.浅谈某产品用50SiMnVB钢横向断裂原因分析[J].精密成形工程,2012,4(1):78-81.
JIANG Chun-mao,PAN Ling,ZHAO Guang-jun,et al.Horizontal Fracture Reason Analysis on a Product of 50SiMnVB Steel[J].Journal of Netshape Forming Engineering,2012,4(1):78-81. |
| 浅谈某产品用50SiMnVB钢横向断裂原因分析 |
| Horizontal Fracture Reason Analysis on a Product of 50SiMnVB Steel |
| 投稿时间：2011-07-26 修订日期：2012-01-10 |
| DOI： |
| 中文关键词: 横向断裂 分析与验证 质量 无损检测 |
| 英文关键词: transverse fracture analysis and verification quality nondestructive testing |
| 基金项目: |
|
| 摘要点击次数: 4185 |
| 全文下载次数: 3252 |
| 中文摘要: |
| 通过对某军工产品用50SiMnVB钢在加热过程中，横向断裂疵病产生的原因机理进行了分析与验证，准确地找到了该问题产生的原因，并在后续生产中增加无损检测技术，可有效地剔除该类缺陷，保证产品质量。 |
| 英文摘要: |
| The mechanism of transverse rupture defects of a military product with 50SiMnVB steel in heating process was analyzed and verified, and the cause was found. Nondestructive testing technology was added in subsequent production, which could be effectively used to eliminate the defects, and guarantee the product quality. |
|